1.2316ESR塑膠模具鋼撫順電渣

博主:adminadmin 2022-10-01 07:42:01 條評論
摘要:(2)供應(yīng)狀態(tài)和硬度淬火,估算狀態(tài)前的預(yù)期,硬度2832hrc(3)典型的化學成分(質(zhì)量評分,%)C0.38,CR16.0撫順電渣,MN0.5,SI(4)Refertothecorrespondingsteelnumberstandardsteelnum...
鋼百科 usteel.net

 ?。?)供應(yīng)狀態(tài)和硬度淬火,估算狀態(tài)前的預(yù)期,硬度2832hrc

1.2316ESR塑膠模具鋼撫順電渣

 ?。?)典型的化學成分(質(zhì)量評分,%)C0.38,CR16.0撫順電渣 ,MN0.5,SI <1.00, MO1.00對標 , Ni <1.00.

  (4) Refer to the corresponding steel number standard steel number 1.2316ESR.

  (5) The soft annealing specification is heated to 740-800 ° C under the protection state, and then cooled to 550 ° C at a rate of 15 ° C/h in the furnace, and then placed in the air to cool.

  (6) The stress elimination specification must be heated to 530 ° C after rough processing.

  (7) The first heating and recovery specifications are 540650 ° C for the first time. Or the foot pressure cooling in the vacuum furnace. R65

  Refer to the fire curve chart to select the ignition temperature and hardness, the ignition 2 times, the recovery temperature> 180℃

 ?。?)在預(yù)熱的物理特性狀態(tài)下:溫度20°C,密度為7800g/cm3,彈性模量MPa。

 ?。?)機械性能測試溫度為20°C,拉伸強度為120MPa,屈服強度為980MPa,截面收縮率為47%,伸長率為12.0%。測試溫度為200°C,拉伸強度為1010MPa,屈服強度為910MPa,截面收縮率為48%,伸長率為10.5%。

 ?。?0)典型的申請示例

 ?、俑g性塑料模具,例如PVC和乙酸鹽有沒有磁性。

 ?、谛枰诔睗竦沫h(huán)境中工作的塑料模具。

 ?、鄞邓芰夏>撸Y(jié)構(gòu)零件等。

鋼百科 usteel.net